Power UltraFET® Reliability Summary
| Part Number Type | Die Type | Package | |||
|---|---|---|---|---|---|
| HUF75329D3S | 78329 | TO-252 | |||
| Test 8098 Lot 1 | |||||
| Stress | Conditions per AEC Q101 |
Results | Sample Size |
Duration | |
| IOL(1) | PD=2.0W, delta Tj=100C | 0 | 77 | 15,000 | Cyc |
| HT Drain Bias | Tc=175C, Vds=80% Rated | 0 | 77 | 1000 | Hrs |
| HT Gate Bias | Tc=175C, Vgs=100% Rated | 0 | 77 | 1000 | Hrs |
| Temp Cycle(1) | -55C, +150C, Air | 0 | 77 | 1000 | Cyc |
| Autoclave(1) | Ta=121C, 15psi | 0 | 77 | 96 | Hrs |
| H3TRB(1) | Ta=85C, RH=85%, Vds=44V | 0 | 77 | 1000 | Hrs |
| Operating Life | Tj=175C, VDS=15V | 0 | 40 | 1000 | Hrs |
| ESD | CDF-AEC-Q101-001 | 0 | 10 | 500VHB 200VMM |
|
| DPA | CDF-AEC-Q101-004 | 0 | 2 | ||
| Thermal Resistance | JESD-24 | 0 | 5 | ||
| Dielectric Integrity | CDF-AEC-Q101-004 | 0 | 5 | ||
| UIS | CDF-AEC-Q101-004 | 0 | 5 | ||
| Temp Cycle(2) | -55C, +150C, Air | 0 | 40 | 400 | Cyc |
| Autoclave(2) | Ta=121C, 15psi | 0 | 40 | 96 | Hrs |
| Note 1: Preconditioning per AEC Q101 (J113) | |||||
| Note 2: Test 8126: Preconditioning per AEC Q101
(J113) using IR peak temp of 260C, followed by 100 cycles at -40C +150C |
|||||
| Part Number Type | Die Type | Package | |||
|---|---|---|---|---|---|
| HUF75329D3S | 78329 | TO-252 | |||
| Test 8098 Lot 2 | |||||
| Stress | Conditions per AEC Q101 |
Results | Sample Size |
Duration | |
| IOL(1) | PD=2.0W, delta Tj=100C | 0 | 77 | 15,000 | Cyc |
| HT Drain Bias | Tc=175C, Vds=80% Rated | 0 | 77 | 1000 | Hrs |
| HT Gate Bias | Tc=175C, Vgs=100% Rated | 0 | 77 | 1000 | Hrs |
| Temp Cycle(1) | -55C, +150C, Air | 0 | 77 | 1000 | Cyc |
| Autoclave(1) | Ta=121C, 15psi | 0 | 77 | 96 | Hrs |
| H3TRB(1) | Ta=85C, RH=85%, Vds=44V | 0 | 77 | 1000 | Hrs |
| Operating Life | Tj=175C, VDS=15V | 0 | 40 | 1000 | Hrs |
| DPA | CDF-AEC-Q101-004 | 0 | 2 | ||
| Temp Cycle(2) | -55C, +150C, Air | 0 | 40 | 400 | Cyc |
| Autoclave(2) | Ta=121C, 15psi | 0 | 40 | 96 | Hrs |
| Note 1: Preconditioning per AEC Q101 (J113) | |||||
| Note 2: Test 8126: Preconditioning per AEC Q101
(J113) using IR peak temp of 260C, followed by 100 cycles at -40C +150C |
|||||
| Part Number Type | Die Type | Package | |||
|---|---|---|---|---|---|
| HUF75329D3S | 78329 | TO-252 | |||
| Test 8098 Lot 3 | |||||
| Stress | Conditions per AEC Q101 |
Results | Sample Size |
Duration | |
| IOL(1) | PD=2.0W, delta Tj=100C | 0 | 77 | 15,000 | Cyc |
| HT Drain Bias | Tc=175C, Vds=80% Rated | 0 | 77 | 1000 | Hrs |
| HT Gate Bias | Tc=175C, Vgs=100% Rated | 0 | 77 | 1000 | Hrs |
| Temp Cycle(1) | -55C, +150C, Air | 0 | 77 | 1000 | Cyc |
| Autoclave(1) | Ta=121C, 15psi | 0 | 77 | 96 | Hrs |
| H3TRB(1) | Ta=85C, RH=85%, Vds=44V | 0 | 77 | 1000 | Hrs |
| Operating Life | Tj=175C, VDS=15V | 0 | 40 | 1000 | Hrs |
| DPA | CDF-AEC-Q101-004 | 0 | 2 | ||
| Temp Cycle(2) | -55C, +150C, Air | 0 | 40 | 400 | Cyc |
| Autoclave(2) | Ta=121C, 15psi | 0 | 40 | 96 | Hrs |
| Note 1: Preconditioning per AEC Q101 (J113) | |||||
| Note 2: Test 8126: Preconditioning per AEC Q101
(J113) using IR peak temp of 260C, followed by 100 cycles at -40C +150C |
|||||